Polyamide nanofiber membranes functionalized with zinc phthalocyanines
- Authors: Goethals, Annelies , Mugadza, Tawanda , Arslanoglu, Yasin , Zugle, Ruphino , Antunes, Edith M , Van Hulle, Stijn W , Nyokong, Tebello , De Clerck, Karen
- Date: 2014
- Subjects: To be catalogued
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/241505 , vital:50945 , xlink:href="https://doi.org/10.1002/app.40486"
- Description: Electrospinning is an efficient method for the production of polyamide nanofiber membranes that are suitable for water filtration. Previous studies have shown that nanofiber membranes have high clean water permeability. The pathogen removal efficiency can be improved by functionalization with (organic) biocides. However, these membranes, like other membranes, are vulnerable to fouling which reduces the filtration efficiency. Therefore the present article investigates the potential of zinc phthalocyanines, which can produce singlet oxygen in the presence of visible light, as a functionalizing agent. The polyamide nanofiber membranes were functionalized with phthalocyanines using both a pre-functionalizing and post-functionalizing method. Only the post-functionalization method shows to result in nanofiber membranes capable of producing singlet oxygen. After 30 min 45% of 1,2-diphenylisobenzofuran (DPBF), used as an oxygen quencher, was removed by reaction with singlet oxygen. This resulted in a removal rate of 0.33 mol DBPF mol−1Zn min−1. During short term leaching tests, phthalocyanines could not be detected.
- Full Text:
- Date Issued: 2014
Effect of the relative humidity on the fibre morphology of polyamide 4.6 and polyamide 6.9 nanofibres
- Authors: De Schoenmaker, Bert , Van de Schueren, Lien , Zugle, Ruphino , Goethals, Annelies , Westbroek, Philippe , Kiekens, Paul , Nyokong, Tebello , De Clerck, Karen
- Date: 2013
- Subjects: To be catalogued
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/242131 , vital:51004 , xlink:href="https://doi.org/10.1007/s10853-012-6934-9"
- Description: To obtain uniform and reproducible nanofibres, it is important to understand the effect of the different electrospinning parameters on the nanofibre morphology. Even though a lot of literature is available on the electrospinning of nanofibres, only minor research has been performed on the effect of the relative humidity (RH). This paper investigates the influence of this parameter on the electrospinning process and fibre morphology of the hydrophilic polyamide 4.6 and the less hydrophilic polyamide 6.9. First, the electrospinning process and deposition area of the nanofibres is examined at 10, 50 and 70 % RH. Subsequently, the effect of the polyamide concentration and solvent ratio on the fibre morphology is investigated using scanning electron microscopy and differential scanning calorimetry. It was found that the nanofibre diameter decreased with increasing RH. This resulted in less stable crystals for polyamide 4.6 while electrospinning of polyamide 6.9 at higher RH led to slightly more stable crystals. In conclusion, the water affinity of a polymer is an important factor in predicting the nanofibre morphology at different humidities.
- Full Text:
- Date Issued: 2013
Polyamide nanofiber membranes functionalized with zinc phthalocyanines
- Authors: Goethals, Annelies , Mugadza, Tawanda , Arslanoglu, Yasin , Zugle, Ruphino , Antunes, Edith M , Hulle, Stijn W H Van , Nyokong, Tebello , Clerck, Karen De
- Language: English
- Type: Article
- Identifier: vital:7313 , http://hdl.handle.net/10962/d1020539
- Description: Electrospinning is an efficient method for the production of polyamide nanofiber membranes that are suitable for water filtration. Previous studies have shown that nanofiber membranes have high clean water permeability. The pathogen removal efficiency can be improved by functionalization with (organic) biocides. However, these membranes, like other membranes, are vulnerable to fouling which reduces the filtration efficiency. Therefore the present article investigates the potential of zinc phthalocyanines, which can produce singlet oxygen in the presence of visible light, as a functionalizing agent. The polyamide nanofiber membranes were functionalized with phthalocyanines using both a pre-functionalizing and post-functionalizing method. Only the post-functionalization method shows to result in nanofiber membranes capable of producing singlet oxygen. After 30 min 45% of 1,2-diphenylisobenzofuran (DPBF), used as an oxygen quencher, was removed by reaction with singlet oxygen. This resulted in a removal rate of 0.33 mol DBPF mol−1Zn min−1. During short term leaching tests, phthalocyanines could not be detected. , Original publication is available at http://dx.doi.org/10.1002/app.40486
- Full Text: false