Oxovanadium (IV)-containing poly (styrene-co-4′-ethenyl-2-hydroxyphenylimidazole) electrospun nanofibers for the catalytic oxidation of thioanisole
- Authors: Walmsley, Ryan S , Litwinski, Christian , Antunes, Edith M , Hlangothi, Percy , Hosten, Eric C , McCleland, Cedric , Nyokong, Tebello , Torto, Nelson , Tshentu, Zenixole R
- Date: 2013
- Subjects: To be catalogued
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/241665 , vital:50959 , xlink:href="https://doi.org/10.1016/j.molcata.2013.07.018"
- Description: The catalytic fibers have been fabricated by the electrospinning of a copolymer of styrene and 2-(2′-hydroxy-4′-ethenylphenyl)imidazole {p(ST-co-VPIM)} followed by a reaction with a methanolic vanadyl solution to afford the oxovanadium(IV)-containing poly(styrene-co-4′-ethenyl-2-hydroxyphenylimidazole) fibers {p(ST-co-VPIM)-VO fibers}. The relationship between polymer concentration and fiber diameter was investigated, and at high concentration (20 wt%) the fibers were quite large (average diameter of 3.8 μm) but as the concentration was reduced fibers of much lower diameter were produced (0.6 μm using 8 wt%). The BET surface area for p(ST-co-VPIM) fibers (0.6 μm diameter) was 47.9 m2 g−1 and functionalization of p(ST-co-VPIM) with vanadyl resulted in an increase in surface area to 60.7 m2 g−1 for p(ST-co-VPIM)-VO. The presence of vanadyl was confirmed by XPS and EPR. The EPR spectral analyses depicted complex speciation of vanadium within these polymer supports. These catalytic fibers were applied under batch and continuous flow conditions for the catalytic oxidation of thioanisole using hydrogen peroxide. The continuous flow method gave excellent and constant conversion throughout the 10 h period studied. The leaching of vanadium from the fiber support was 4% over the 10 h period indicating a significant stability of the material.
- Full Text:
- Date Issued: 2013
CdTe quantum dots functionalized with 4-amino-2, 2, 6, 6-tetramethylpiperidine-N-oxide as luminescent nanoprobe for the sensitive recognition of bromide ion
- Authors: Adegoke, Oluwasesan , Hosten, Eric C , McCleland, Cedric , Nyokong, Tebello
- Date: 2012
- Subjects: To be catalogued
- Language: English
- Type: text , article
- Identifier: http://hdl.handle.net/10962/244393 , vital:51253 , xlink:href="https://doi.org/10.1016/j.aca.2012.01.040"
- Description: A novel bromide ion-selective modified nanoprobe sensor based on 4-amino-2,2,6,6-tetramethylpiperidine-N-oxide (4AT)-functionalized CdTe quantum dots (QDs-4AT) has been developed. Fluorescence quenching of the QDs by 4AT was observed. The functionalized QDs-4AT nanoprobe allowed a highly sensitive determination of bromide ion via analyte-induced change in the photoluminescence (fluorescence recovery) of the modified QDs. A detection limit of 0.6 nM of bromide ion was obtained, while the interfering effect of other inorganic cations and anions was investigated to examine the selectivity of the nanoprobe. The linear range was between 0.01 and 0.13 μM. Combined fluorescence lifetime and electron paramagnetic resonance measurements confirmed electron transfer processes between bromide ion and QDs-4AT.
- Full Text:
- Date Issued: 2012